Influence of the Cooling Rate on the Morphology of Spheroidic Graphite Obtained by the CO2 Process

Autores

  • Mauro Carlos Souza Universidade Estadual da Zona Oeste - UEZO Departamento de Metalurgia
  • Antonio Carlos de Araújo Santos Depatment of Metallurgical Processes at the West Zone State University, UEZO
  • Wilma Clemente de Lima Pinto Depatment of Metallurgical Processes at the West Zone State University, UEZO
  • Mila Rosendal Avelino Department of Mechanical Engineering at the Rio de Janeiro State University, UERJ,

DOI:

https://doi.org/10.47385/cadunifoa.v8.n22.146

Palavras-chave:

solidification, casting, ductile iron cast, morphology

Resumo

The mechanical properties of cast metallic materials are strongly influenced by processing parameters, such as percentage of silicate, sand granulometry, and metallurgical processing. The ductile iron cast produced by the CO2 process depends on variables that determine the behavior of the material in service, such as the cooling rate and chemical composition. This study evaluated the influence of the cooling rate on the spheroidic graphite. In order to determine this effect, a simulation was performed in specimens with 20, 25, and 30 mm in thickness, through the characterization of type, measurement of nodule size, and distribution of nodules. Chemical analysis and mechanical resistance tests were performed. The 25 mm thick specimen showed the best behavior among the three thicknesses evaluated, presenting the formation of many small nodules and a small amount of larger nodules in the center.

Downloads

Não há dados estatísticos.

Biografia do Autor

Mauro Carlos Souza, Universidade Estadual da Zona Oeste - UEZO Departamento de Metalurgia

Engenheiro Quimico, Mestrado em Eng Nuclear (COPPE/UFRJ, Doutorado em Metalurgia e Materiais (COPPE/UFRJ) Pos doc em Irradiação de Alimentos. Prof. Adjunto da UERJ e da UEZO, no Depto. de Metalurgia

Antonio Carlos de Araújo Santos, Depatment of Metallurgical Processes at the West Zone State University, UEZO

Graduação em Tecnólogo em Processos Metalúrgicos pelo Centro Universitário da Zona Oeste, Brasil(2010)
Professor Celetista do Centro Universitário da Zona Oeste , Brasil

Wilma Clemente de Lima Pinto, Depatment of Metallurgical Processes at the West Zone State University, UEZO

Doutorado em Química Inorgânica pela Universidade Federal do Rio de Janeiro, Brasil(2003)
Professor Adjunto doutor I da Universidade do Grande Rio , Brasil

Mila Rosendal Avelino, Department of Mechanical Engineering at the Rio de Janeiro State University, UERJ,

Doutorado em Engenharia Mecânica pela Universidade Federal do Rio de Janeiro, Brasil(2000)
Professor Adjunto da Universidade do Estado do Rio de Janeiro , Brasil

Referências

ASKELAND, D.R., GRUPTA, S.S., Effect of Nodule Count and Cooling Rate on the Matrix of Nodular Cast Iron. Transations of the American Foundrymen’s Society. Vol. 83, p.313-320, 1975.

ASTM A247-67. Standard Test Method for Evaluating The Microstructure of Graphite in Iron Casting, 1998.

ASTM A536-84. Standard Specification for Ductile Iron Castings, 2009.

CAMPOS FILHO, M. P., DAVIES, G. J., Solidificação e Fundição de Metais e suas Ligas,1a Ed., S. Paulo, LTC/EDUP, 1978.

CHAVES FILHO, L. M., PIESKE, A., CASTRO, C. P. Avaliação do Comportamento de Alguns Inoculantes para Ferros Fundidos Cinzentos. Joinville, Soc.Educ.Tupy, p.167, 1975.

DAWSON, J.P. The Future Role of Inoculation Technology. In: Bcira, Foundry Technology for the 80’s. Birminghan, p.3.1-3.18, 1979.

DOS SANTOS, M. A., MÜLLER, A., Velocidade de Extração de Calor sobre as Macro e Miroestruturas de um Ferro Fundido Nodular, quase Eutético. In: XXXII Congresso Anual da ABM, S. Paulo, Julho de 1977.

HASSE, S., Guß und Gefügefehler, Berlin, Schiele & Schön, p. 209, 1999.

MUZUNDAR, K.M., WALLACE, J.F. Transations of the American Foundrymen’s Society. Vol.81, p.412-423, 1973.

RESMAN, R.W., LOPER J.R., C.R. Transations of the American Foundrymen’s Society, Vol.75, p.1-9, 1967.

SADOSHA, J.R., GRUZLESKI, J.E., The Metallurgy of Cast Iron, New York, George Publishing Co., 1975,

SANTOS, A.B.S. Aspectos Relativos à Morfologia da Grafita em Seções Espessas de Ferro Fundido Nodular. In: Congr. Ilafa de fundición de Hierro y Acero, Rio de Janeiro, p.131-143, 1976.

SANTOS, A.B.S., BRANCO, C.H.C., Metalurgia dos Ferros Fundidos Cinzentos e Nodu-lares. São Paulo, IPT (PUBLIC.1100), p.241, 1977.

WEIZER, P. F., BATES, C. E., WALLACE, J. F. Cleveland, Malleable Founder’s Soc.., p.81, 1967..

Downloads

Publicado

10-08-2013

Como Citar

SOUZA, Mauro Carlos; ARAÚJO SANTOS, Antonio Carlos de; LIMA PINTO, Wilma Clemente de; AVELINO, Mila Rosendal. Influence of the Cooling Rate on the Morphology of Spheroidic Graphite Obtained by the CO2 Process. Cadernos UniFOA, Volta Redonda, v. 8, n. 22, p. 37–41, 2013. DOI: 10.47385/cadunifoa.v8.n22.146. Disponível em: https://revistas.unifoa.edu.br/cadernos/article/view/146. Acesso em: 24 nov. 2024.

Edição

Seção

Tecnologia e Engenharias